Crack length data of the circular specimens under torsional cyclic loads with outer initial precrack
Published: 10 March 2025| Version 1 | DOI: 10.17632/hbn8k4m6r7.1
Contributors:
, Pavel Michel Almaguer Zaldivar, Description
The response of the materials under the action of cyclic loads is always a topic of interest of the engineers and researchers. In this dataset is showed the results for the torsional fatigue test of the cylindrical cross section specimens. A longitudinal crack was induced in the outter diameter. The specimen material is AISI 1015 steel. Fatigue test was realized in the torsional testing machine described in the literature. The asymmetry ratio used was -1. It is showed the crack size ai respect to the number of cycles Ni and pictures of the cross section after the failure.
Files
Institutions
Universidad de Holguin Oscar Lucero Moya
Categories
Fatigue Life, Fatigue Crack, Fatigue Behavior