Dataset for Copper Yttrium Titanium Oxide (CYTO) ceramic material on analysis of Dielectric properties at different Temperature
Description
In the present study, synthesis of novel ceramic material copper yttrium titanium oxide CuY2Ti4O12 is proposed by ordinary solid state reaction method due to lower sintering temperature by semi wet route. Dataset of the paper highlights the effects of sintering temperature on dielectric properties and crystalline phase of CYTO materials. Dielectric constant and dielectric loss of CuY2Ti4O12 (CYTO) ceramic materials were studied with respect to temperature and frequency CuY2Ti4O12 (CYTO) ceramic by semi-wet route synthesis, the X-ray diffraction (XRD) pattern was used to confirm the crystalline plane which exhibit high intensity of CYTO ceramic material at 15000 cps, calculated by X-ray diffraction pattern. The dielectric constant increases with increasing temperature and decreases with frequency. The high value of dielectric constant was found to be εˈ ≈ 12×103 at 495 K, 100 Hz, at low frequency due to the presence of interfacial polarization in the ceramic materials.
Files
Steps to reproduce
N4L PSN 1735 and Rigaku Mini flex 600 instrument used for characterization of materials.