Data for: The effect of salt loading on chloride-induced stress corrosion cracking of 304L austenitic stainless steel under atmospheric conditions

Name: Data for: The effect of salt loading on chloride-induced stress corrosion cracking of 304L austenitic stainless steel under atmospheric conditions
Creator: mark wenman
Published: 2020-03-31T18:47:45.786Z
Keywords: Austenitic Stainless Steel, Atmospheric Corrosion, Stress Corrosion Cracking, Chloride, Transgranular Stress Corrosion Cracking

wenman, mark

doi:10.17632/mrwrphjvjr.1

Data for: The effect of salt loading on chloride-induced stress corrosion cracking of 304L austenitic stainless steel under atmospheric conditions

Published: 31 March 2020| Version 1 | DOI: 10.17632/mrwrphjvjr.1

Contributor:

mark wenman

Description

Processed data: Excel spread sheet of corroded area, crack velocity and crack density data.

Data for: The effect of salt loading on chloride-induced stress corrosion cracking of 304L austenitic stainless steel under atmospheric conditions