Manufacture and mechanical characterization of sandwich composites made from a polyurethane resin and jute sewing 3D-fabrics reinforcements

Description

This article aims to develop a new type of sandwich composite with jute sewing 3D-fabrics structure. The sandwich composite was a lightweight composite with reasonable mechanical properties and was manufactured by compression molding. The jute sewing 3D-fabrics was produced by sewing jute yarns having configurable structures using Kevlar fiber threads. The composites had been subjected to compression, flexural and impact tests and their fracture surfaces had been characterized by scanning electron microscopy. The compression and impact properties of the blank composites and the sandwich composites were compared. In terms of flexural performance, three types of flexural failure modes were analyzed.